AL-COT(Hot Dip Aluminum Coated Steel Sheet)

Categories:

Hot-dip aluminum coated steel sheet combines the mechanical properties of cold-rolled steel sheet with aluminum’s high resistance retention, heat reflection, and superior rust resistance.

USAGE

Automotive components

muffler, exhaust pipes, fuel tanks

 

Home Electrical Appliances

Electric stove, gas range, bread machine, electric stove, toaster, frying pan, dryer

 

Heating equipment

heat exchanger, stovepipe, pre-heater, dryer, duct

 
Construction

Walls and roofs of chemical factories, fireproof wall

 
Other

Steam cover, other chemical equipment

DESCRIPTION

Superior Heat Resistance

Lengthy exposure to temperatures up to 450 degrees Celsius causes very little change in ALCOT and does not affect its attractive surface brightness, compared with galvanized steel sheet and cold-rolled steel sheet.

 

Heat Resistance Test Results

Test conditions: Naked eye comparison the sheet after two rounds of test procedures (Heating (1.5 Hr), maintaining (5 Hr), cooling (17 Hr))

category 300℃ 350℃ 400℃ 450℃ 500℃ 550℃ 600℃
ALCOT
×
GALVALUME
△~×
×
×
×
GI
△~×
×
×
×
×
×

○ : No change △ : Luster down × : Tums blackish

 

Heat Resistance Test Results

When heated, an oxide film is formed on the surface as the alloy layer is activated, protecting its surface.

Superior Heat Reflectivity

The highly elegant surface of ALCOT reflects about 80% of the heat at a temperature of 450 degrees Celsius. Its reflection rate goes up to 95% where infrared rays are present. This makes ALCOT the ideal choice for producing the heat reflector plates in toasters, ovens, gas ranges and oil stoves.

 

Heat Reflectivity

Type ALCOT GI
100℃×24hr
80%
80%
450℃×24hr
80%
15%

Coating Layers

 

Types of ALCOT steel sheet are categorized by the components of the molten pot. Applications are as follows

 
Classification Type Ⅰ Alumininized Type Ⅱ Alumininized
components of the molten pot.
Al-Si(8~10%)
Al
Components of the alloy layer
Type Ⅰ Aluminized
Type Ⅱ Aluminized
Application
Heat resistance treatment
Weather resistance
(construction material)
 
Post-treatment

 

The highly elegant surface of ALCOT reflects about 80% of the heat at a temperature of 450 degrees Celsius. Its reflection rate goes up to 95% where infrared rays are present. This makes ALCOT the ideal choice for producing the heat reflector plates in toasters, ovens, gas ranges and oil stoves.

Heat Reflectivity

Chromated Oiled Chromated & Oiled No Treatment
Chromating

– Average : 11.5 mg/m² (one side)
– Range : 6.8~18.9mg/m² (one side)
 

Oiling

– Slightly : 500~800mg/m² (both side)
– Normal : 1,000~1,400mg/m² (both side)
– Heavy : 1,400~2,000mg/m² (both side)
 
Grade and Symbol
Class JIS G3314 ASTM A 463 ASTM A 463-96a EN 10154
Commercial Quality (Type1)
CQ
SA1C
CQ
CS TYPE A
DX51D
CS TYPE B
DX52D
CS TYPE C
Drawing Quality (Type1)
DQ1
SA1A
ADQ
-
DX53D
DQ2
SA1D
DQ
FS
DX54D
DDS
DX55D
DQ3
SA1E
DQSK
EDDS
-
EDDQ
-
EDDQ
EDDS
-
Structural Quality (Type1)
Grade A
SAC31
SQ-A
Grade230
-
Grade B
SAC35
SQ-B
Grade255
S250GD
S280GD
Grade C
SAC41
SQ-C
Grade275
S320GD
Grade D
SAC45
SQ-D
Grade340 Class1
S350GD
Grade340 Class2
Grade F
-
Grade340 Class3
-
Grade E
-
Grade550
-
 
Mechanical Properties
Class Tensile Strength (㎏/㎟) Yield Point (㎏/㎟)
Thickness (㎜)
Elongation(%)
Thickness(㎜)
T≤0.5
0.5< t
t≤0.5
0.5< t≤1.2
1.2
Commercial Quality
Grade A
SAC31, SQ-A
31min
21min
21min
20min
20min
20min
Grade B
SAC35, SQ-B
35min
25min
25min
20min
20min
20min
Grade C
SAC41, SQ-C
41min
30min
30min
18min
18min
18min
Grade D
SAC45, SQ-D
45min
37min
37min
18min
18min
18min

Coating Layers

 

-KS D 3544
-JIS G 3314
-ASTM A 525 (FOR ASTM A463)
-EN 10143